  • AZS RAMMING MASS

AZS RAMMING MASS

Catalog: Zirconia monolithics material | 2022-01-25

AZS ramming mass is made of crushed fused cast AZS brick particles as aggregate materials mixed with other auxiliary materials. It reserves the advantage of fused cast AZS bricks such as good corrosion resistance to molten glass and metals, low porosity and stable properties.

Product Details

AZS RAMMING MASS

Physical and chemical index

 

Item

AZSR-50V

 

Chemical

Composition

Al2O3

48

ZrO2

30

SiO2

20

Others

2

Bulk density g/cm3

3.2

Crystallographic analysis after being sintered at

Corundum, zirconium oxide

Thermal conductivity

Good

Anti-corrosion property

Excellent at 1300

particle diameter of grain

0-5mm

Application temperature

Cold/low temperature

Quantity ofwater

8- 10%

Solidification

Water (ceramic)

Packaging

25kg/bag

Quality guarantee period

12 months


Used for

Under bottom paving,

USAGE: 1. Open the bag to check if the coagulant agent is dampened or hardened, and then spread the coagulant agent uniformly into the bag;

2.Mix certain amount of the mass according to on-site assumption. When it mixes well, add room temperature water by a ratio of 6-7%, or adjust the ratio according to local climatic condition and water content of the mixture. Blend it till there is no raw ramming mass left or till that it will break into pieces instantly when it falls to the ground after one unlooses his grip ofthe mass from the height of 0.33 meters;

3. The  construction  site  and  bonder  should  be  clean  and  without  sundries.  The leftover well-mixed mass should be covered with plastic sheet film or placed in shady  and  cool place.  The  mass  that  is  not  dry  and  hard  can be  used  again; otherwise,  it  should  be  crushed  and  used  together  with  other  raw  material  or abandoned.

4.Mix with water to make the material like slurry then press smooth by vibrating.

CONCRETING TIME: BEGINNING TIME: 0:15~2:00 HOURS

FINISHING TIME: 3:00~6:00 HOURS

HEATING TIME:AFTER 150:00 HOURS

THIS MATERIAL IS WITHOUT PHOSPHORUS,

AND DOES NOT POLLUTE THE ENVIROMENT.